mechanochemically synthesized mesoporous alumina an

Current Location : Home > mechanochemically synthesized mesoporous alumina an

  • Alumina decorated TiO 2 nanotubes with ordered mesoporous

    Alumina (Al 2 O 3 ) decorated anatase TiO 2 nanotubes with ordered mesoporous pore walls (Al 2 O 3 /meso-TiO 2 nanotubes) are successfully synthesized through vacuum pressure induction technology and then combined with the thermal decomposition of a mesoporous TiO 2 sol precursor inside the cylindrical nanochannels of an anodic aluminium oxide (AAO) template.

    Chat Online
  • One‐Pot Synthesis of Potassium‐Functionalized Mesoporous γ

    Apr 14 2008 · Basically super Potassium‐functionalized mesoporous γ‐alumina solid superbases that have a high base strength (H −) of 27.0 a well‐expressed mesoporous structure and which are efficient in the isomerization of 1‐hexene are synthesized by a one‐pot method.The success of this method can be ascribed to the flexible application of K 2 CO 3 as a pH adjustor and close control of the

    Chat Online
  • Facile strategy for synthesis of mesoporous crystalline γ

    The facile synthesis of mesoporous γ-alumina is developed through the partial hydrolysis of Al(NO 3) 3 aqueous solution with (NH 4) 2 CO 3 without organic surfactants. In this synthesis the stable NH 4 NO 3 /Al species (AN/Al) hybrid containing Keggin-Al 13 polycations is first prepared which is the key for the successful formation of mesoporous γ-alumina. XRD 27 Al MAS NMR TEM and N 2

    Chat Online
  • A Novel Synthesis Route of Mesoporous γ-Alumina from

    Mesoporous gamma-aluminas (γ-Al 2 O 3) were synthesized starting from an unusual precursor of polyoxohydroxide aluminum (POHA). This precursor was obtained from aluminum oxidation in alkaline water-ethanol solvent in the presence of d-glucose that induces the formation of a gel which leads to the POAH powder after ethanolic treatment.

    Chat Online
  • Synthesis of mesoporous gamma-alumina nanorods using a

    Mesoporous gamma-Al2O3 nanorods were synthesized by a reverse microemulsion (water in oil w/o) technique using an aqueous-based alumina sol the anionic surfactant AOT (sodium bis(2-ethylhexyl sulfosuccinate)) the non-ionic co-surfactant Span 80 (sorbitan monooleate) and cyclohexane as an organic solvent. The gamma-Al2O3 phase was obtained at 500 degrees C with a slight transformation

    Chat Online
  • A Novel Synthesis Route of Mesoporous γ-Alumina from

    Mesoporous gamma-aluminas (γ-Al 2 O 3) were synthesized starting from an unusual precursor of polyoxohydroxide aluminum (POHA). This precursor was obtained from aluminum oxidation in alkaline water-ethanol solvent in the presence of d-glucose that induces the formation of a gel which leads to the POAH powder after ethanolic treatment.

    Chat Online
  • 3D Interconnected Mesoporous Alumina with Loaded

    Mar 27 2018 · In this study ordered mesoporous alumina (OMA) with interconnected mesopores and surface acidic property is synthesized through a solvent evaporation induced co-assembly process using poly (ethylene oxide)-b-polystyrene (PEO-b-PS) diblock copolymer as a template and aluminium acetylacetonate (Al (acac) 3 ) as the aluminium source.

    Chat Online
  • Templated synthesis of mesoporous aluminas by graft

    Aluminas synthesized with PVC-g-POEM graft copolymer exhibited higher CO2 adsorption capacities (0.7 mol CO 2/kg sorbent) than aluminas synthesized without graft copolymer (0.6 mol CO2/kg sorbent). The adsorption capacity of alumina strongly depends on its structure and calcination temperature amorphous (400 °C) > γ phase (800 °C) > α

    Chat Online
  • One‐Pot Synthesis of Potassium‐Functionalized Mesoporous γ

    Apr 14 2008 · Basically super Potassium‐functionalized mesoporous γ‐alumina solid superbases that have a high base strength (H −) of 27.0 a well‐expressed mesoporous structure and which are efficient in the isomerization of 1‐hexene are synthesized by a one‐pot method.The success of this method can be ascribed to the flexible application of K 2 CO 3 as a pH adjustor and close control of the

    Chat Online
  • Optical and Electrical Properties of Mechanochemically

    Aug 08 2008 · Nanocrystalline p-type semiconductor copper aluminum oxide (CuAlO 2) has been synthesized by mechanical alloying using freshly prepared Cu 2 O and α-Al 2 O 3 nanocrystals in toluene medium. A study on structural property performed with different alloying and post annealing durations by X-ray diffraction (XRD) reveals the formation of single phase with average crystallite size

    Chat Online
  • Mechanochemically synthesized mesoporous alumina An

    Mechanochemically synthesized mesoporous alumina An advanced sorbent for post-processing concentration of 131 I for cancer therapy J Chromatogr A . 2020 Feb 81612 460614. doi 10.1016/j roma.2019.460614.

    Chat Online
  • Mesoporous Titania‐Alumina Mixed Oxide A Heterogeneous

    Oct 22 2018 · Mesoporous titania‐alumina mixed oxide (MTAMO) was synthesized by sol‐gel pathway using sodium dodecyl sulfate as a structure directing agent and successfully employed as a highly efficient nanocatalyst for the synthesis of 2‐substituted benzimidazoles benzothiazoles and benzoxazoles using 30 H 2 O 2 as a green oxidant. The described methodology offers the benefits

    Chat Online
  • Homogeneously Dispersed Ceria Wiley Online Library

    Mar 26 2010 · Homogeneously dispersed ceria nanocatalyst can be synthesized and stabilized with ordered mesoporous alumina by a one‐step sol–gel method. This novel material possesses high thermal stability and exhibits 100 conversion at room temperature for

    Chat Online
  • Bead-Shaped Mesoporous Alumina Adsorbents for Adsorption

    Here we report the uniform Bead-Shaped Mesoporous Alumina (BSMA) with tunable particle size for use as an adsorbent for removal of toxic ammonia. The BSMA particles with tunable diameters were synthesized by means of a sol–gel reaction of Al(NO3)3∙9H2O as an alumina precursor in the presence of chitosan as a template.

    Chat Online
  • Synthesis of Mesoporous γ-Al2O3 with Spongy

    Over the past decades extensive efforts have been devoted to modulating the textural properties morphology and microstructure of γ-Al2O3 since the physiochemical properties of γ-Al2O3 have close correlations with the performance of hydrotreating catalysts. In this work a spongy mesoporous γ-alumina (γ-Al2O3) was synthesized using Al-based metal-organic frameworks (Al-MOFs) as

    Chat Online
  • Template-Free Fabrication of Mesoporous Alumina

    Mechanochemically Synthesized Mesoporous Alumina An Advanced Sorbent for Post-Processing Concentration of 131I for Cancer Therapy The SS-alumina was synthesized from aluminium nitrate

    Chat Online
  • Mesoporous Titania‐Alumina Mixed Oxide A Heterogeneous

    Oct 22 2018 · Mesoporous titania‐alumina mixed oxide (MTAMO) was synthesized by sol‐gel pathway using sodium dodecyl sulfate as a structure directing agent and successfully employed as a highly efficient nanocatalyst for the synthesis of 2‐substituted benzimidazoles benzothiazoles and benzoxazoles using 30 H 2 O 2 as a green oxidant. The described methodology offers the benefits

    Chat Online
  • High-surface-area corundum by mechanochemically induced

    Oct 25 2019 · High-purity corundum (α-Al2O3) nanoparticles could enable applications such as more stable catalyst supports or precursors for high-strength ceramics. Milling of corundum only produces micrometer-scale particles and direct synthesis from other aluminum oxides that would be likely starting materials such as γ-Al2O3 fails because of the high activation barrier for converting the lattice

    Chat Online
  • A Novel Synthesis Route of Mesoporous γ-Alumina from

    ABSTRACT. Mesoporous gamma-aluminas (γ-Al 2 O 3) were synthesized starting from an unusual precursor of polyoxohydroxide aluminum (POHA).This precursor was obtained from aluminum oxidation in alkaline water-ethanol solvent in the presence of d-glucose that induces the formation of a gel which leads to the POAH powder after ethanolic treatment.

    Chat Online
  • Facile Synthesis of Mesoporous Alumina with Tunable

    Mesoporous alumina (MA) with interesting morphologies of flower or three‐dimensional hierarchical spheres like nanostructures were synthesized in the absence of any template. Hydrothermal synthesis strategy was applied for synthesis of mesoporous γ‐ alumina with tunable properties like BET surface area pore volume pore size and superior

    Chat Online
  • Synthesis of mesoporous carbon using gelatin as source of

    2.2. Preparation of mesoporous carbons Mesoporous carbon material was synthesized by using SBA-15 mesoporous material as a silica template (particle size 0 1 µm pore diameter 7-8 nm surface area 550 m2/g pore volume 1 0 cm3/g) and gelatin as the carbon source.

    Chat Online
  • Synthesized mesoporous silica and calcium aluminate cement

    This study evaluated the effect of different types of filler in a resin-based pit and fissure sealant on fluoride release recharge and lactic acid neutralization. Resin-based sealant was incorporated with 5 w/w of the following fillers calcium aluminate cement (CAC) synthesized mesoporous silica (SI) a CAC and SI mixture (CAC SI) glass-ionomer powder (GIC) and acetic

    Chat Online
  • Mechanochemically synthesized high alumina cement and

    Nano-meter sized high alumina cement (HAC) powders were synthesized by mechanochemical treatment of Al2O3 and CaCO3 in weight ratios 7 3 and 8 2. This paper compares the calcined high alumina cement obtained by mechanically activated precursor mix for 1 2 and 3 h.

    Chat Online
  • Bead-Shaped Mesoporous Alumina Adsorbents for Adsorption

    Here we report the uniform Bead-Shaped Mesoporous Alumina (BSMA) with tunable particle size for use as an adsorbent for removal of toxic ammonia. The BSMA particles with tunable diameters were synthesized by means of a sol–gel reaction of Al(NO3)3∙9H2O as an alumina precursor in the presence of chitosan as a template.

    Chat Online
  • A Novel Synthesis Route of Mesoporous γ-Alumina from

    ABSTRACT. Mesoporous gamma-aluminas (γ-Al 2 O 3) were synthesized starting from an unusual precursor of polyoxohydroxide aluminum (POHA).This precursor was obtained from aluminum oxidation in alkaline water-ethanol solvent in the presence of d-glucose that induces the formation of a gel which leads to the POAH powder after ethanolic treatment.

    Chat Online
  • Structural characterization of mesoporous silica

    Jul 14 2009 · Mesoporous silica nanofibers were synthesized within the pores of the anodic aluminum oxide template using a simple sol–gel method. Transmission electron microscopy investigation indicated that the concentration of the structure-directing agent (EO 20 PO 70 EO 20) had a significant impact on the mesostructure of mesoporous silica nanofibers.Samples with alignment of nanochannels along

    Chat Online
  • Mesoporous materialWikipedia

    A mesoporous material is a material containing pores with diameters between 2 and 50 nm according to IUPAC nomenclature. For comparison IUPAC defines microporous material as a material having pores smaller than 2 nm in diameter and macroporous material as a material having pores larger than 50 nm in diameter.. Typical mesoporous materials include some kinds of silica and alumina that have

    Chat Online

Related Posts

  • evaluation of waste heat recovery technologies for the
  • cast iron properties processing and applications
  • important considerations for refractory dryouts startupstesting of refractories and refractoring testing of
  • life cycle benefits of recycled material in highway
  • high efficiency long life hot stove nippon steelblast furnace bf
  • refractory ladle lining brick manufacturers suppliersladle castable
  • material flow planning
  • $2 5 billion magnesia chrome brick market
  • 기술 용어 사전 네이버 블로그us10526542b2
  • china refractory manufacturer ramming mass refractoryan introduction to the types of monolithic refractories
  • remedial measures and campaign life of a blast furnace
  • refractory lining material for iron steel making onrefractory ramming mass

Product Center

  • Alumina Hollow Ball Bricks
  • Corundum Spinel Castable
  • High Alumina Refractory Cement
  • High Alumina Low Cement Castable
  • High Alumina Refractory Ramming Mass
  • Trough Refractory Castable
  • Magnesium Iron Spinel Brick
  • Mullite Brick
  • Zirconium Mullite Brick

Hot Products

  • Light Weight Silica Insulation Brick
  • Zirconia Hollow Sphere Brick
  • Corundum Refractory Castable
  • Heavy Alkali Resistant Castable
  • High Alumina Low Cement Castable
  • High Alumina Self Flowing Castable
  • Micro Expansion Refractory Plastic
  • Phosphate Refractory Mud
  • Magnesia Zircon Brick

Images Show

About Us

Rongsheng's main products are various types of unshaped refractory products, which are widely used in metallurgy, nonferrous metals, building materials, electric power, petrochemical and other industries.

Rongsheng pays attention to technological innovation and product research and development, and has established close cooperative relations with many universities and scientific research institutes.

Zhengzhou Rongsheng Company © Copyrights. Sitemap